    沙伯基礎 SABICLEXAN EXL1112T 透光性  耐紫外線

    沙伯基礎 SABICLEXAN EXL1112T 透光性 耐紫外線

    LEXAN EXL1112T有良好的透光性,抗沖擊性,耐紫外線輻射及其制品的尺寸穩定性和良好的成型加工性能,使其比建筑業傳統使用的無機玻璃具有明顯的技術性能優勢。

    全國24小時銷售熱線:

    13829200144
    產品介紹


    美國沙伯基礎SABIC LEXAN EXL1112T PC物性表參數


    SABIC Lexan? EXL1112T PC物性表
    The property table is provided by www.cn-plas.com, welcome to download, reprint please indicate the source!
    Material Notes:
    Lexan EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. Lexan EXL1112 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
    Physical Properties物理性質
    Metric公制數據
    English英制數據
    Comments測試方法
    Specific Gravity比重
    1.18 g/cc
    1.18 g/cc
    ASTM D 792
    Density密度
    1.19 g/cc
    0.0430 lb/in3
    ISO 1183
    Moisture Absorption at Equilibrium吸濕平衡
    0.15 %
    0.15 %
    23°C / 50% RH; ISO 62
    Water Absorption at Saturation吸水率
    0.35 %
    @Temperature 23.0 °C
    0.35 %
    @Temperature 73.4 °F
    ISO 62
    Linear Mold Shrinkage, Flow線性收縮率/流動
    0.0040 - 0.0080 cm/cm
    @Thickness 3.20 mm
    0.0040 - 0.0080 in/in
    @Thickness 0.126 in
    SABIC Method
    Linear Mold Shrinkage, Transverse 
    0.0040 - 0.0080 cm/cm
    @Thickness 3.20 mm
    0.0040 - 0.0080 in/in
    @Thickness 0.126 in
    SABIC Method
    Melt Flow熔體流動速率
    16 g/10 min
    @Load 1.20 kg,
    Temperature 300 °C
    16 g/10 min
    @Load 2.65 lb,
    Temperature 572 °F
    [cm^3/10 min] Melt Volume Rate; ISO 1133

    17 g/10 min
    @Load 1.20 kg,
    Temperature 300 °C
    17 g/10 min
    @Load 2.65 lb,
    Temperature 572 °F
    ASTM D 1238
    Mechanical Properties力學性能
    Metric公制數據
    English英制數據
    Comments測試方法
    Hardness,硬度 H358/30 
    95.0 MPa
    13800 psi
    ISO 2039-1
    Tensile Strength at Break斷裂拉伸強度
    55.0 MPa
    7980 psi
    50 mm/min; ISO 527

    58.0 MPa
    8410 psi
    Type I, 50 mm/min; ASTM D 638
    Tensile Strength, Yield屈服拉伸強度
    57.0 MPa
    8270 psi
    50 mm/min; ISO 527

    58.0 MPa
    8410 psi
    Type I, 50 mm/min; ASTM D 638
    Elongation at Break斷裂伸長率
    100 %
    100 %
    50 mm/min; ISO 527

    109 %
    109 %
    Type I, 50 mm/min; ASTM D 638
    Elongation at Yield屈服伸長率
    5.0 %
    5.0 %
    50 mm/min; ISO 527

    5.8 %
    5.8 %
    Type I, 50 mm/min; ASTM D 638
    Tensile Modulus拉伸模量
    2.15 GPa
    312 ksi
    1 mm/min; ISO 527

    2.28 GPa
    331 ksi
    50 mm/min; ASTM D 638
    Flexural Yield Strength彎曲屈服強度
    85.0 MPa
    12300 psi
    2 mm/min; ISO 178

    95.0 MPa
    13800 psi
    1.3 mm/min, 50 mm span; ASTM D 790
    Flexural Modulus彎曲彈性模量
    2.24 GPa
    325 ksi
    2 mm/min; ISO 178

    2.32 GPa
    336 ksi
    1.3 mm/min, 50 mm span; ASTM D 790
    Izod Impact, Notched 懸臂梁缺口沖擊強度  
    6.67 J/cm
    @Temperature -30.0 °C
    12.5 ft-lb/in
    @Temperature -22.0 °F
    ASTM D 256

    7.47 J/cm
    @Temperature 23.0 °C
    14.0 ft-lb/in
    @Temperature 73.4 °F
    ASTM D 256
    Izod Impact, Notched 懸臂梁缺口沖擊強度 (ISO) 
    20.0 kJ/m2
    @Temperature -30.0 °C
    9.52 ft-lb/in2
    @Temperature -22.0 °F
    80*10*3; ISO 180/1A

    55.0 kJ/m2
    @Temperature 23.0 °C
    26.2 ft-lb/in2
    @Temperature 73.4 °F
    80*10*3; ISO 180/1A
    Izod Impact, Unnotched 懸臂梁無缺口沖擊強度(ISO)  
    NB
    @Temperature 23.0 °C
    NB
    @Temperature 73.4 °F
    80*10*3; ISO 180/1U

    NB
    @Temperature -30.0 °C
    NB
    @Temperature -22.0 °F
    80*10*3; ISO 180/1U
    Charpy Impact Unnotched夏比缺口試樣沖擊
    NB
    @Temperature 23.0 °C
    NB
    @Temperature 73.4 °F
    Edgew 80*10*3 sp=62mm; ISO 179/1eU

    NB
    @Temperature -30.0 °C
    NB
    @Temperature -22.0 °F
    Edgew 80*10*3 sp=62mm; ISO 179/1eU
    Charpy Impact, Notched夏比缺口沖擊
    2.50 J/cm2
    @Temperature -30.0 °C
    11.9 ft-lb/in2
    @Temperature -22.0 °F
    V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA

    6.00 J/cm2
    @Temperature 23.0 °C
    28.6 ft-lb/in2
    @Temperature 73.4 °F
    V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
    Impact Test 沖擊試驗數據
    69.0 J
    @Temperature 23.0 °C
    50.9 ft-lb
    @Temperature 73.4 °F
    Instrumented Impact Total Energy; ASTM D 3763
    Thermal Properties熱性能
    Metric公制數據
    English英制數據
    Comments測試方法
    CTE, linear, Parallel to Flow線性熱膨脹系數
    72.0 μm/m-°C
    @Temperature -40.0 - 40.0 °C
    40.0 μin/in-°F
    @Temperature -40.0 - 104 °F
    ASTM E 831

    75.0 μm/m-°C
    @Temperature 23.0 - 80.0 °C
    41.7 μin/in-°F
    @Temperature 73.4 - 176 °F
    ISO 11359-2
    CTE, linear, Transverse to Flow線性熱膨脹系數/橫向  
    75.0 μm/m-°C
    @Temperature 23.0 - 80.0 °C
    41.7 μin/in-°F
    @Temperature 73.4 - 176 °F
    ISO 11359-2

    75.6 μm/m-°C
    @Temperature -40.0 - 40.0 °C
    42.0 μin/in-°F
    @Temperature -40.0 - 104 °F
    ASTM E 831
    Deflection Temperature at熱變形溫度0.46 MPa (66 psi) 
    136 °C
    @Thickness 3.20 mm
    277 °F
    @Thickness 0.126 in
    unannealed; ASTM D 648

    136 °C
    @Treatment Temperatur 80.0 °C,
    Time 14400 sec
    277 °F
    @Treatment Temperatur 176 °F,
    Time 4.00 hour
    edgew. Annealed; ISO 75/Be
    Deflection Temperature at熱變形溫度1.8 MPa (264 psi) 
    125 °C
    257 °F
    Edgew 120*10*4 sp=100mm; ISO 75/Ae

    123 °C
    @Thickness 3.20 mm
    253 °F
    @Thickness 0.126 in
    unannealed; ASTM D 648
    Vicat Softening Point維卡軟化點
    144 °C
    291 °F
    Rate B/50; ASTM D 1525

    144 °C
    291 °F
    Rate B/50; ISO 306

    145 °C
    293 °F
    Rate B/120; ISO 306
    UL RTI, Electrical 相對溫度指數
    130 °C
    266 °F
    UL 746B
    UL RTI, Mechanical with Impact機械沖擊熱指數
    120 °C
    248 °F
    UL 746B
    UL RTI, Mechanical without Impact無機械沖擊熱指數
    125 °C
    257 °F
    UL 746B
    Oxygen Index氧指數
    32 %
    32 %
    LOI; ISO 4589
    Glow Wire Test灼熱絲測試
    850 °C
    @Thickness 0.800 mm
    1560 °F
    @Thickness 0.0315 in
    Glow Wire Flammability Index; IEC 60695-2-12

    875 °C
    @Thickness 1.00 mm
    1610 °F
    @Thickness 0.0394 in
    Glow Wire Ignitability Temperature; IEC 60695-2-13

    875 °C
    @Thickness 3.00 mm
    1610 °F
    @Thickness 0.118 in
    Glow Wire Ignitability Temperature; IEC 60695-2-13

    960 °C
    @Thickness 3.00 mm
    1760 °F
    @Thickness 0.118 in
    Glow Wire Flammability Index; IEC 60695-2-12


    LEXAN PC EXL1112t是幾乎無色的玻璃態的無定形聚合物,有很好的光學性。PC高分子量樹脂有很高的韌性,懸臂梁缺口沖擊強度為600~900J/m,未填充牌號的熱變形溫度大約為130°C ,玻璃纖維增強后可使這個數值增加10°C。PC的彎曲模量可達2400MPa以上,樹脂可加工制成大的剛性制品。低于100°C 時,在負載下的蠕變率很低。PC耐水解性差,不能用于重復經受高壓蒸汽的制品。

    SABIC的LEXAN EXL1112T PC樹脂是聚碳酸酯(PC)硅氧烷共聚物樹脂是一種高流動不透明注射成型(IM)等級。該樹脂具有良好的低溫(-20 C)延展性,并具有良好的加工性能,并與標準PC相比,具有更短的IM周期時間。LEXAN EXL1112樹脂是一種廣泛應用于各種不透明顏色的產品,可能是廣泛應用的優秀候選產品。樹脂可以透明和有限的不透明的顏色。強度高、耐疲勞性、尺寸穩定、蠕變也?。ǜ邷貤l件下也極少有變化).
    LEXAN EXL1112T有良好的透光性,抗沖擊性,耐紫外線輻射及其制品的尺寸穩定性和良好的成型加工性能,使其比建筑業傳統使用的無機玻璃具有明顯的技術性能優勢。

    PC 基礎創新塑料(美國) 慨述
    PC是聚碳酸酯的簡稱,聚碳酸酯的英文是Polycarbonate,簡稱PC工程塑料,PC材料其實就是我們所說的工程塑料中的一種,作為被世界范圍內廣泛使用的材料,PC有著其自身的特性和優缺點,PC是一種綜合性能優良的非晶型熱塑性樹脂,具有優異的電絕緣性、延伸性、尺寸穩定性及耐化學腐蝕性,較高的強度、耐熱性和耐寒性;還具有自熄、阻燃、無毒、可著色等優點,在你生活的各個角落都能見到PC塑料的影子,大規模工業生產及容易加工的特性也使其價格極其低廉。PC材料分子鏈中含有碳酸酯基,酯基的結構可分為脂肪族、芳香族、脂肪族-芳香族等多種類型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的機械性能較低,從而限制了其在工程塑料方面的應用。目前僅有芳香族聚碳酸酯獲得了工業化生產。俗稱防彈膠,是一種無色透明的無定性熱塑性材料,五大工程塑料之一,產量僅次于PA。
     


    PC 基礎創新塑料(美國) 性質
    化學性質:聚碳酸酯(PC)是碳酸的聚酯類,碳酸本身并不穩定,但其衍生物(如光氣,尿素,碳酸鹽,碳酸酯)都有一定穩定性。按醇結構的不同,可將聚碳酸酯分成脂族和芳族兩類。
    脂族聚碳酸酯。如聚亞乙基碳酸酯,聚三亞甲基碳酸酯及其共聚物,熔點和玻璃化溫度低,強度差,不能用作結構材料;但利用其生物相容性和生物可降解的特性,可在藥物緩釋放載體,手術縫合線,骨骼支撐材料等方面獲得應用。聚碳酸酯耐弱酸,耐弱堿,耐中性油。聚碳酸酯不耐紫外光,不耐強堿。
    PC是一種線型碳酸聚酯,分子中碳酸基團與另一些基團交替排列,這些基團可以是芳香族,可以是脂肪族,也可兩者皆有。雙酚A型PC是最重要的工業產品。
    PC是幾乎無色的玻璃態的無定形聚合物,有很好的光學性。PC高分子量樹脂有很高的韌性,懸臂梁缺口沖擊強度為600~900J/m,未填充牌號的熱變形溫度大約為130°C ,玻璃纖維增強后可使這個數值增加10°C。PC的彎曲模量可達2400MPa以上,樹脂可加工制成大的剛性制品。低于100°C 時,在負載下的蠕變率很低。PC耐水解性差,不能用于重復經受高壓蒸汽的制品。
    PC主要性能缺陷是耐水解穩定性不夠高,對缺口敏感,耐有機化學品性,耐刮痕性較差,長期暴露于紫外線中會發黃。和其他樹脂一樣,PC容易受某些有機溶劑的侵蝕。
    PC材料具有阻燃性,耐磨??寡趸?。
    物理性質:
    密度:1.18-1.22 g/cm^3 線膨脹率:3.8×10^-5 cm/°C 熱變形溫度:135°C 低溫-45°C
    聚碳酸酯無色透明,耐熱,抗沖擊,阻燃BI級,在普通使用溫度內都有良好的機械性能。同性能接近聚甲基丙烯酸甲酯相比,聚碳酸酯的耐沖擊性能好,折射率高,加工性能好,不需要添加劑就具有UL94 V-0級阻燃性能。但是聚甲基丙烯酸甲酯相對聚碳酸酯價格較低,并可通過本體聚合的方法生產大型的器件。
    聚碳酸酯的耐磨性差。一些用于易磨損用途的聚碳酸酯器件需要對表面進行特殊處理。
    分類
    防靜電PC,導電PC,加纖防火PC,抗紫外線耐候PC,食品級PC,抗化學性PC。
     

    PC 基礎創新塑料(美國) 優點
    1、具高強度及彈性系數、高沖擊強度、使用溫度范圍廣;2、高度透明性及自由染色性;3、.高;4、耐疲勞性佳;5、耐候性佳;6、電氣特性優;7、無味無臭對人體無害符合衛生安全;8、成形收縮率低、尺寸安定性良好。
     
    PC 基礎創新塑料(美國) 應用范圍:
    光學照明:用于制造大型燈罩、防護玻璃、光學儀器的左右目鏡筒等,還可廣泛用于飛機上的透明材料。
    電子電器:聚碳酸酯是優良的E(120℃)級絕緣材料,用于制造絕緣接插件、線圈框架、管座、絕緣套管、電話機殼體及零件、礦燈的電池殼等。也可用于制作尺寸精度很高的零件,如光盤、電話、電子計算機、視頻錄象機、電話交換器、信號繼電器等通訊器材。聚碳酸酯薄摸還被廣泛用作電容器、絕緣皮包、錄音帶、彩色錄象磁帶等。
    機械設備:用于制造各種齒輪、齒條、蝸輪、蝸桿、軸承、凸輪、螺栓、杠桿、曲軸、棘輪,也可作一些機械設備殼體、罩蓋和框架等零件。
    醫療器材:可作醫療用途的杯、筒、瓶以及牙科器械、藥品容器和手術器械,甚至還可用作人工腎、人工肺等人工臟器。
    其它方面:建筑上用作中空筋雙壁板、暖房玻璃等;在紡織行業用作紡織紗管、紡織機軸瓦等;日用方面作奶瓶、餐具、玩具、模型、LED燈外殼和手機外殼等。
     